UPILEX®-RN High Heat-Resistant Film
Mechanical Properties | Properties | | Unit | 25RN | | 50RN | 75RN | 125RN | Test Method | | Tensile Strength (MD) | MD | MPa | 402 | 373 | 379 | 349 | ASTM D882 | | TD | 409 | 402 | 399 | 368 | | Elongation (MD) | MD | % | 172 | 142 | 153 | 138 | ASTM D882 | | TD | 168 | 136 | 144 | 130 | | Tensile Modulus (MD) | MD | MPa | 3932 | 3491 | 3716 | 3658 | ASTM D882 | | TD | 3932 | 3569 | 3785 | 3736 | | Tear Strength-Initiation [Graves] (MD) | MD | N | 344 | 647 | 929 | 1391 | JIS C 2318 | | TD | 374 | 677 | 955 | 1384 | | Folding endurance [MIT] | MD | Cycles | >100,000 | >100,000 | 16,000 | 1,100 | ASTM D2176 | | TD | >100,000 | >100,000 | 22,000 | 1,300 | | Density | g/cm3 | 1.39 | ASTM D1505 | | Coefficient of Kinetic Friction (film-to-film) | --- | 0.4 | ASTM D1894 |
Electrical Properties | Properties | Unit | 25RN | 50RN | 75RN | 125RN | Test Conditions | Test Method | | Dielectric Strength | kV | 6.5 | 12.0 | 13.8 | 15.6 | 50Hz | ASTM D149 | | Dielectric Constant | --- | 3.2 | 3.2 | 3.4 | 3.5 | 1kHz | ASTM D150 | | Dissipation Factor | --- | 0.0018 | 0.0017 | 0.0023 | 0.0018 | 1kHz | ASTM D150 | | Volume Resistivity | Ω - cm | 4.3*1016 | 6.7*1016 | 5.3*1016 | 5.9*1016 | DC100V | ASTM D257 | | Surface Resistivity | Ω | 9.1*1016 | 1.9*1017 | 1.8*1017 | 9.8*1016 | DC100V | ASTM D257 |
Thermal Properties | Properties | Unit | 50RN | 75RN | 125RN | Test Conditions (Test Method) | | MD | TD | MD | TD | MD | TD | | Heat shrinkage | % | 0.1 | 0.01 | | | | | 200°C, 2Hours JIS C2318 | | Thermal Linear Expansion Coeficient (50 - 200°C) | ppm/K | 12 | 20 | | | | | Values determined by minute linear expansion tester at 5°C/min. temperature increments | | Melting Point | °C | None | | | Specific Heat | kJ(kg·K) | 1.09 | Differential ScanningCalorimeter | | Temperature Index | °C | 270 | Heat Treatment: 20,000Hours | | Glass Transition Temperature | °C | 285 | Dynamic Viscosity | | Flammability | --- | UL94 V-0 | UL94 File No.48133 | | Oxygen Index | % | 55 | JIS K7201 | | Thermal Conductivity | W/(m·K) | 0.24 | Laser Flash Method |
Chemical Resistant Properties | Properties | 25RN | 75RN | 125RN | Test Conditions | Test Method | | Strength | Elongation | Modulus | | | | Retained(%) | Retained(%) | Retained(%) | | | | Resistanceto: | | | 10% Sodium Hydroxide | | | Glatial Acetic Acid | | | P-Cresol | | | Water | PH=1.0 | | | | PH=4.2 | | | | PH=8.9 | | | | PH=10.0 | | | | | | | | 85 | | 110 | | 55 | | 100 | | 100 | | 100 | | 100 | | | | | | | | | 105 | | 115 | | 50 | | 110 | | 115 | | 115 | | 115 | | | | | | | | | | Immersion at 25°C for 5 days | | Immersion at 110°C for 5 weeks | | Immersion at 200°C for 3weeks | | Immersion at 100°C for 2 weeks | | Immersion at 100°C for 2 weeks | | Immersion at 100°C for 2 weeks | | Immersion at 100°C for 4 days | | ASTM D882 | | Water Absorption | | | | | Immersion inwater at 23°C for 24 hours | | ASTM D570 | | Gas Permeability | | | Water Vapor | | | Oxygen | | | Nitrogen | | | Carbon Dioxide | | | Helium | | | | | | | | 22g/m2/mil | | 100ml/m2/mil | | 30ml/m2/mil | | 115ml/m2/mil | | 2200ml/m2/mil | | | | | | | | | | | | | | 38°C, RH90% for 24 Hours |  | 30°C, 1 atm, for 24 Hours | | |
Chemical Resistant Properties (2) | Chemicals | Immersion Conditions | Dimensional Stability (%) | | 25RN | 75RN | 125RN | | MD | TD | MD | TD | MD | TD | | Ferric Chloride (37%) | At room Temperature for 10 minutes | -0.00 | -0.00 | -0.00 | -0.00 | -0.00 | -0.00 | | Cupric Chloride (37%) | At room Temperature for 10 minutes | +0.00 | -0.00 | +0.00 | +0.00 | +0.00 | +0.00 | | 5% Sodium Hydroxide | At 60°C for 10minutes | +0.00 | -0.00 | +0.00 | +0.00 | +0.01 | +0.01 | | | At 60°C for 30minutes | -0.00 | -0.02 | +0.00 | -0.00 | +0.01 | -0.01 | | 2N-Hydrochloric Acid | At room Temperature for 10 minutes | -0.00 | -0.00 | -0.00 | +0.00 | -0.00 | +0.00 | | 2N-Sodium Hydroxide | At room Temperature for 10 minutes | +0.00 | +0.01 | -0.00 | +0.00 | +0.01 | +0.01 | | Isopropane | At room Temperature for 10 minutes | +0.00 | +0.01 | +0.00 | +0.00 | +0.00 | +0.00 | | Toluene | At room Temperature for 10 minutes | +0.01 | +0.01 | +0.01 | +0.00 | +0.00 | +0.00 | | Methyl Ethyl Ketone | At room Temperature for 10 minutes | +0.01 | +0.01 | +0.00 | -0.00 | +0.00 | -0.00 | | Methylene Chloride/Trichloroethane (Mixed) | At room Temperature for 10 minutes | -0.00 | +0.01 | +0.00 | -0.00 | -0.00 | -0.00 |
|
 |
|