UBETAC® APAO
Application fields
1. Hot melt adhesive and sealant
- Diaper
- Product assembly for electric and electronics
- Product assembly for automobile
- Product assembly for architecture material>
- Packaging
- Non woven, etc.
2.Backing compound of carpet tile
3. Filling, flooding and coating of cable
- Sticky filling compound
- Filling and coating compound of extrusion type
4. Modifier of plastics and elastomers
- Soft PP (replacement of PVC)
- Modifier of thermoplastic elastomer (SEBS, etc.)
5. Wax blend
- Rope grease
- Anti-rust wax
- Modifier of wax
6. Modifier of asphalt for roofing membrance
- Flexibility at low temperature and prevention of flow at high temperature
7. Modifier of asphalt pavement
- Flexibility at low temperature and prevention of flow at high temperature
8. Paper lamination
9. Binder of filler compound
Table Polymer composition and feature
Composition | | Viscosity (190°C) | | Propylene
homo | Propylene/ethylene | Propylene/
butene-1 | Feature | Low
ethylene | Medium
ethylene | High
ethylene | High
butene-1 | | 400 CPS | UT2104 | | UT2304 | | | | Easy to mix
and apply | | | | Good mechanical
properties | | | 1,500 CPS | UT2115 | UT2215 | UT2315 | | UT2715 | | 3,000 - 3,500 CPS | | | UT2330 | UT2535 | UT2730 | | 8,000 - 8,500 CPS | UT2180 | UT2280 | UT2385 | UT2585 | UT2780 | | Feature | | Hard |  | Soft | | High softening point (S.P.) | Low S.P. | | Good heat resistance | Good low temp. property | | Low S.P. High cohesive strength |
*Both UBETAC® APAOs produced by URC in Japan and REXTAC® APAOs produced by Rexene Products Company in U.S.A. have the same nomenclature and properties between the same grade number, though initials of UT and RT are different.
Example: UBETAC UT2585=REXTAC RT2585
*Please don't hesitate to contact us, if you have something to ask or request.
Table Grade of APAO
| | UT2104 | UT2115 | UT2180 | UT2215 | UT2280 | UT2304 | UT2315 | UT2330 | UT2385 | UT2535 | UT2585 | UT2715 | UT2730 | UT2780 | Melt viscosity cps
(190°C) | 400 | 1500 | 8000 | 1500 | 8000 | 400 | 1500 | 3000 | 8500 | 3500 | 8500 | 1500 | 3000 | 8000 | Needle penetration
dmm | 17 | 15 | 10 | 20 | 15 | 25 | 25 | 20 | 20 | 45 | 40 | 30 | 30 | 30 | Ring & Ball softening
point °C | 147 | 152 | 157 | 143 | 146 | 138 | 138 | 141 | 141 | 129 | 129 | 107 | 110 | 110 | Solid density g/cm3
(25°C) | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.86 | 0.87 | 0.87 | 0.87 | Melt density g/cm3
(190°C) | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.74 | 0.75 | 0.75 | 0.75 | Glass transition
temp °C | -17 | -14 | -13 | -22 | -21 | -32 | -28 | -28 | -27 | -36 | -35 | -28 | -26 | -26 |
The above values are typical data.